SABIC® LLDPE 6335BE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bhgGur_SABIC-LLDPE-6335BE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 6335BE is a hexene linear low density polyethylene resin for cast film applications. The product has been specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast films produced from SABIC® LLDPE 6335BE exhibit excellent optical properties, toughness, puncture resistance, tear strength and stiffness. The suffix E denotes European origin. Application SABIC® LLDPE 6335BE resin is recommended for use in non cling layers in pallet stretch wrap (pre-stretch), high performance draw down films and other mono layer and coextruded film applications where high strength is required. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Elastic Recovery - Cast Film (20.0 µm) | 46 | % | ASTM D5459 |
| Protrusion Puncture Resistance - Cast Film (20.0 µm) | 1.40 | J | ASTM D5748 |
| Stress Retention - Cast Film (20.0 µm) | 75 | % | ASTM D5459 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Impact - Cast Film (20.0 µm) | 14.0 | J/cm | ISO 7765-2 |
| Tear Strength - TD 1(20.0 µm) | 227.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 117 | °C | ISO 306/A |
| Melting Temperature (DSC) | 126 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 87 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 3.1 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Properties are determined on 20 µm cast stretch film produced on a 2 m commercial cast stretch film line: melt temperature 270°C, chill roll temperature 20°C and line speed 450 m/min. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 - 300 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 161 Z | RTP Company | PP, Unspecified | RTP |
| Aaroprene® GFIPP 2010 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| Comco PA 6 G high impact | Comco-Plastic GmbH | Nylon 6 | Comco |
| DENISAB 2010 | Vamp Tech | ABS | DENISAB |
| IDI BMC B30 (Glass Content 25%) | IDI Composites International | TS, Unspecified | IDI BMC |