TEKALOY™ G70NH
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bdNgE3_TEKALOY-G70NH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TEKALOY™ G70NH is a Polycarbonate + ABS (PC+ABS) product. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.50 to 0.60 | % | |
| Across Flow | 0.50 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 57.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 55 | % | ASTM D638 |
| Flexural Modulus | 2450 | MPa | ASTM D790 |
| Flexural Strength | 93.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 220 to 260 | °C | |
| Middle Temperature | 210 to 250 | °C | |
| Front Temperature | 200 to 240 | °C | |
| Nozzle Temperature | 220 to 260 | °C | |
| Processing (Melt) Temp | 215 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 98.1 to 157 | MPa |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® M TM3RST (Series: MC/RS) | KRAIBURG TPE | TPE | THERMOLAST® M |
| Vi-Chem PVC VNC101E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TPUCO® TPU-C95 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Dynaprene® SE0058A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| GELOY™ CR7520 resin | SABIC Innovative Plastics | ASA | GELOY™ |