EPO-TEK® 330
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bbgKRk_EPO-TEK-330.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® 330 is a two component, high-temperature grade, electrically and thermally insulating epoxy for semiconductor, electronics, fiber optics and medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 90.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 3.9E-5 | cm/cm/°C | |
| -- 3 | 1.8E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.535 | ||
| Transmittance | |||
| 500 nm | > 51.0 | % | |
| 600 nm | > 88.0 | % | |
| 700 to 1600 nm | > 97.0 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 369 | °C | TGA |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 2.10 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.68 | % | |
| 250°C | 1.1 | % | |
| 300°C | 1.8 | % |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 5 | Amber | ||
| -- 6 | Clear/Transparent | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.15 | g/cm³ | |
| Viscosity 7(23°C) | 0.35 to 0.55 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 360 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 87 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 3.74 | ||
| Volume Resistivity (23°C) | > 2.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.011 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroelastomer FT 2350 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Huafon JF-P-5180 / JF-I-5118 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| IROGRAN® A 92 E 4246 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Pier One POM AH500P-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | Pier One POM |
| TORZEN® HV125A NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |