Tenopom® POM A3 LF PRTA010 PR315
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Tenopom® POM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yG2t9Q_Tenopom-POM-A3-LF-PRTA010-PR315.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyacetal copolymer with low viscosity in natural color, easy processing, suitable for injection parts where it needs to be easily completed. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/1.05 kg) | 1.0 to 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 67.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 78 | % | ASTM D638 |
| Flexural Modulus | 2780 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 163 | °C | |
| 1.8 MPa, Unannealed | 94.0 | °C | |
| Peak Melting Temperature | 177 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+14 | ohms·cm | ASTM D257 |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 220 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PC PC0703 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| TECHNO ABS 620 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 2001Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| ALTECH® PA66 A 1000/109 BK1008-13LS | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Electrafil® PA6 C BK | Techmer Engineered Solutions | Nylon 6 | Electrafil® |