High Density Polyethylene Extra high molecular weight, copolymer Extrusion-Blow Molding

Characteristics

The KPOL HD K-9.0/956, is a high molecular weight high-density polyethylene, copolymer. Suitable for large parts blow molded up to 50 lts. Exhibit an good impact resistance and excellent stress cracking resistance (ESCR).

Applications

General large parts blow molded, Industrial Tanks and 50-gallon drums.

The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

General Information
Additive	Antioxidant
Features	Antioxidant Copolymer Food Contact Acceptable Good Impact Resistance High Density High ESCR (Stress Crack Resist.) High Molecular Weight
Uses	Blow Molding Applications Drums Tanks
Agency Ratings	FDA 21 CFR 177.1520(c)
Processing Method	Blow Molding Extrusion Extrusion Blow Molding

Physical	Nominal Value	Unit	Test Method
Density	0.956	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/21.6 kg)	9.0	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance ¹
50°C, 1.91 mm, 10% Igepal CO-630	500	hr	ASTM D1693B
50°C, 3.18 mm, 100% Igepal CO-630	> 1000	hr	ASTM D1693A

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	62		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	32.0	MPa	ASTM D638
Tensile Elongation (Break)	800	%	ASTM D638
Flexural Modulus - Tangent	1.32	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength	450	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -60.0	°C	ASTM D746
Vicat Softening Temperature	124	°C	ASTM D1525
Melting Temperature	131	°C	DSC
Heat Deflection Temperature	74	°C	ASTM D648

Note Message
1 .	Grooved Specimen

Resin Grade	Manufacturer	Category	Trademark
SAXALEN™ PPH335T20	SAX Polymers	PP Homopolymer	SAXALEN™
TECHNYL STAR™ AFX 218 V60 NATURAL	Solvay Engineering Plastics	Nylon 66	TECHNYL STAR™
Sindustris PP R7701	Sincerity Australia Pty Ltd.	PP, Unspecified	Sindustris PP
Fainplast PVC PH 60/A	Fainplast Compounds S.r.l	PVC, Flexible	Fainplast PVC
Plasmer 7050N/1002	HYUNDAI EP Co., Ltd.	TPE	Plasmer