Cellophane™ 450PUT
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Cellophane™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yvrBNU_Cellophane-450PUT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Non Heat-Sealable Tape Base Films Uncoated regenerated cellulose film (RCF) with high mechanical strength. 400/450/500PUT have been developed for use as a base for the manufacture of adhesive tapes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.50 | ||
| vs. Itself - Static | 0.70 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 31 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 31 µm | > 3000 | MPa | |
| 1% Secant, TD : 31 µm | > 1500 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 31 µm | 125 | MPa | |
| TD : Yield, 31 µm | 70.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 31 µm | 22 | % | |
| TD : Break, 31 µm | 70 | % | |
| Oxygen Transmission Rate (Wet) (23°C, 31 µm, 0.0% RH) | 1.00 | cm³/m²/24 hr | ASTM F1927 |
| Yield (31.2 µm) | 22.2 | m²/kg | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TULAMID® PA-IR | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| WPP PP PRC25MF1.2C | Washington Penn Plastic Co. Inc. | PP, Unspecified | WPP PP |
| Nylene® 5213 HS | Custom Resins Group | Nylon 6 | Nylene® |
| ALTECH® PA66 A 2030/589 GF30 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Catalyst LV/1LR | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |