Braskem PE HS5103
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b2LFfr_Braskem-PE-HS5103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HS5103 is a high molecular weight high-density polyethylene, copolymer. Suitable for large parts blow molded an L-ring drum. Exhibit an good impact resistance and excellent stress cracking resistance (ESCR). Application: L-ring drum and general large parts blow molded. Process: Blow Molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.951 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 3.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1 | ASTM D1693 | ||
| 2.00mm, 10% Igepal, molded, F50 | 500 | hr | ASTM D1693 |
| 2.00mm, 100% Igepal, molded, F50 | > 800 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 35.0 | MPa | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (-40°C) | 475 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 70.0 | °C | ASTM D648 |
| Injection instructions |
|---|
| Recommended Blow Molding Conditions: Barrel: 180°to 190°C Die: 200° to 220°C Mold Temperature Range: 5°C to 25°C |
| Note Message | |
|---|---|
| 1 . | 0.3mm notched-plaques |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 700 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| GAPEX® HP RPP30EB88HB | Ferro Corporation | PP Homopolymer | GAPEX® HP |
| Hostacom M2 T02 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| POLYCOMPO PE 6200B | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |
| Tunhe PBS TH804 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBS | Tunhe PBS |