Petrothene® L3035
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AnWV37_Petrothene-L3035.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene L3035 is a fractional melt index LDPE resin that exhibits an exceptional balance of optics, modulus, puncture, tear and shrink characteristics. Typical applications include collation shrink film, shrink bundling, pallet shrink film, frozen food packaging, overwraps and heavy duty films where clarity and stiffness are important. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.929 | g/cm³ | ASTM D1558 |
| Melt Mass-Flow Rate (MFR) | 0.40 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| MD | 303 | MPa | ASTM D882 |
| TD | 338 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 14.5 | MPa | ASTM D882 |
| TD : Yield | 15.2 | MPa | ASTM D882 |
| MD : Fracture | 32.4 | MPa | ASTM D882 |
| TD : Fracture | 28.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 470 | % | ASTM D882 |
| TD : Fracture | 550 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 230 | g | ASTM D1922 |
| TD | 310 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 70 | ASTM D2457 | |
| Haze | 7.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance | 1.80 | J | ASTM D5748 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Data obtained from 2.0 mil film produced on a 2" extruder with a 4" die, 410°F Melt Temperature, 3:1 BUR, 0.060" die gap at 50 lb/hr. |
| Note Message | |
|---|---|
| 1 . | Base Resin Density |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 34S5070 | The Matrixx Group, Inc. | PBT | Matrixx |
| Spartech Polycom PE2A-005 | Spartech Polycom | HDPE, HMW | Spartech |
| Nymax™ ND633 GF Natural | PolyOne Corporation | Nylon 6 | Nymax™ |
| LNP™ STAT-KON™ RFD04 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| Sylvin 9657-85 Clear Blue 8399 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |