FREQTIS® P1231A
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | FREQTIS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b2HWKG_FREQTISP1231A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FREQTIS®P1231A is a polyphenylene sulfide (PPS) product, which contains 65% glass and mineral. It is available in North America, Europe or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Forms |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Transverse flow : 2.00mm | 0.50 | % | Internal method |
| Flow : 2.00mm | 0.40 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.70 | % | ISO 527-2 |
| Flexural Modulus | 16000 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Flexural Strain | 0.90 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color Number | KD3051 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.6 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | Internal method | ||
| Flow | 2.0E-5 | cm/cm/°C | Internal method |
| Lateral | 3.0E-5 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 9.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 10 | kV/mm | IEC 60243-1 |
| Relative Permittivity | |||
| 1 MHz | 12.0 | IEC 60250 | |
| 3.00 GHz 1 | 12.0 | Internal method | |
| Dissipation Factor 2(3.00 GHz) | 3.0E-3 | Internal method | |
| Arc Resistance | 108 | sec | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (310°C, 1000 sec^-1) | 280000 | mPa·s | ISO 11443 |
| Note Message | |
|---|---|
| 1 . | Cavity Resonator Method |
| 2 . | Cavity Resonator Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 2671 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| NuSil MED2-6300 | NuSil Technology | Silicone | NuSil |
| Infino TK-2046H | SAMSUNG SDI CO., LTD. | PCT | Infino |
| LNP™ THERMOCOMP™ RZ0069 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Plaskon CMU-880-MA | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |