NuSil MED-2174

Category:	Rubber , Rubber
Manufacturer:	NuSil Technology
Trademark:	NuSil
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	yU3SeQ_NuSil-MED-2174.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
NuSil Technology's unrestricted materials may be considered for long-term implant applications (greater than 29 days). HCRs can be used for extrusion of tubing and profi les (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus. HCRs with a peroxide cure system have a long history in implant applications. The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts. Comments: UNCATALYZED

Message

NuSil Technology's unrestricted materials may be considered for long-term implant applications (greater than 29 days).

HCRs can be used for extrusion of tubing and profi les (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus.

HCRs with a peroxide cure system have a long history in implant applications. The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts.

Comments: UNCATALYZED

General Information
Uses	Washer Pipe fittings Balloon application Profile Medical/nursing supplies
Agency Ratings	USP Class VI
Processing Method	Extrusion Resin transfer molding Profile extrusion molding Compression molding Calendering

Mechanical	Nominal Value	Unit
Tensile Strength (200% Strain)	2.24	MPa

Thermoset	Nominal Value	Unit
Post Cure Time (205°C)	4.0	hr

Additional Information	Nominal Value	Unit
Cure System	Peroxide
Plasticity: 105 mils

Uncured Properties	Nominal Value	Unit
Density	1.15	g/cm³
Curing Time (116°C)	0.083	hr

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore A)	50
Tensile Strength	8.27	MPa
Tensile Elongation at Break	780	%
Tear Strength	39.4	kN/m

Resin Grade	Manufacturer	Category	Trademark
BMC 902	Bulk Molding Compounds, Inc.	Polyester, TS	BMC
Grilamid® 2S 25 W 20 HL X black 9992	EMS-GRIVORY	Nylon 610	Grilamid®
Idemitsu PS SEHI-128	Idemitsu PS	PS (HIPS)	Idemitsu PS
LNP™ THERMOCOMP™ RZ006S compound	SABIC Innovative Plastics	Nylon 66	LNP™ THERMOCOMP™
ULTEM™ 2310 resin	SABIC Innovative Plastics	PEI	ULTEM™