PC-ABSCOM™ B300
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polymer Compounders Limited |
| Trademark: | PC-ABSCOM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | az7lvw_PC-ABSCOM-B300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC-ABSCOM B300 is a PC/ABS alloy with superior heat distortion and impact properties. Typical applications include automotive interior and safety equipment housings. Honda HES D2501 approved. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.70 | % | |
| Equilibrium, 23°C, 50% RH | 0.22 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Yield, -40°C | 63.0 | MPa | ISO 527-2 |
| Yield, 80°C | 20.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 4.3 | % | ISO 527-2/50 |
| Yield, -20°C | 6.3 | % | ISO 527-2 |
| Break | 35 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 47 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 48 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 131 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| CLTE - Flow | 9.5E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 70.0 | °C | |
| Injection Velocity | 60 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285B TFE 13 SI 2 | RTP Company | Nylon 610 | RTP |
| Viprene™ P55D-22U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| BorSafe™ HE3490-DS-H | Borealis AG | PE, Unspecified | BorSafe™ |
| CALP FR913-1 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Infino XI-4208 | SAMSUNG SDI CO., LTD. | Nylon, Unspecified | Infino |