NEXT PCR ABS M35-300PCR
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | NEXT Specialty Resins, Inc. |
| Trademark: | NEXT PCR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ePpA8z_NEXT-PCR-ABS-M35-300PCR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEXT PCR ABS M35-300PCR is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in North America for injection molding. Important attributes of NEXT PCR ABS M35-300PCR are:
Typical applications include:
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1930 | MPa | ASTM D790 |
| Tensile Strength | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 76.7 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® CB 01/2 HSE | PolyPacific Pty. Ltd. | PP Copolymer | Retpol® |
| TABOREN PH 89 T 10 | SILON s.ro | PP Homopolymer | TABOREN |
| TAROLOY 70 | Taro Plast S.p.A. | PC+PBT | TAROLOY |
| Nymax™ GF1200 A43 NATURAL | PolyOne Corporation | Nylon 66 | Nymax™ |
| Sylvin 8250-75UV White 1575 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |