Solef® 3208/0150
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | A. Schulman Europe |
| Trademark: | Solef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aw7CiI_Solef-3208-0150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low friction coefficient - Injection |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.79 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 5.00 | cm³/10min | ISO 1133 |
| 230°C/5.0 kg | 16.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3 sec) | 76 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 1900 | MPa | ISO 178 |
| Flexural Stress 2 | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 68.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 169 | °C | ISO 306/A50 |
| -- | 136 | °C | ISO 306/B50 |
| Thermal Conductivity | 0.24 | W/m/K | ISO 22007-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.800 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.60 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.20 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 900 | °C | IEC 60695-2-13 |
| 3.00 mm | 900 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210SG30 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| NILFLEX® 8 K30T | Taro Plast S.p.A. | PP Copolymer | NILFLEX® |
| DynaChar™ C112 | Polymer Dynamix | Polyolefin, Unspecified | DynaChar™ |
| ESPRENE EPDM 505A | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Karina IVORY PVC COMP. -E 105852-35/ 1-A-IS-L | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |