Bormed™ RG835MO
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormed™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kbN1KH_Bormed-RG835MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bormed RG835MO is a specially modified transparent polypropylene random copolymer with high meltflow. This polymer grade is intended for production of medical and medical-related articles. This grade is modified with internal lubricant for products requiring a low surface friction. and is characterized by easy processability, high transparency, high gloss, controlled low friction, and good stiffness-impact balance at ambient temperature. In addition it can be sterilized with ethylene oxide or steam and has an excellent chemical resistance. In addition to its good physical properties and excellent transparency, this grade also yields products with good printability, which are easily demoulded. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 to 2.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 27.5 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 12 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 82.0 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 to 50.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection molded specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT1055-624 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| SCANAMID 66 A53^ F43 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Sindustris PBT GP2307FG | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Huafon HF-4095A | Huafon Group Co., Ltd. | TPU-Polyether | Huafon |
| OnFlex™ S KA 60A-3S1769 | PolyOne Corporation | TPE | OnFlex™ |