LNP™ THERMOTUF™ WF008N compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | abE5GS_LNPTHERMOTUFWF008Ncompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
40% glass fiber reinforced, high strength, high flow, for NMT application |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 7.00 | cm³/10min | ISO 1133 |
| 275°C/5.0 kg | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow | 0.27 | % | Internal method |
| Transverse flow | 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10600 | MPa | ASTM D638 |
| -- | 11000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 126 | MPa | ASTM D638 |
| Yield | 131 | MPa | ISO 527-2/5 |
| Fracture 3 | 126 | MPa | ASTM D638 |
| Fracture | 131 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2/5 |
| Fracture 5 | 3.0 | % | ASTM D638 |
| Fracture | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 9200 | MPa | ASTM D790 |
| -- 7 | 9700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 208 | MPa | ISO 178 |
| Fracture, 50.0mm span 8 | 194 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 13 | kJ/m² | ISO 179/2C |
| 23°C | 14 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 85 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 130 | J/m | ASTM D256 |
| 23°C | 140 | J/m | ASTM D256 |
| -30°C 9 | 13 | kJ/m² | ISO 180/1A |
| 23°C 10 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 11 | 69 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 207 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 209 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 203 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 205 | °C | ASTM D1525 13 |
| -- | 203 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 1.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 1.2E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 9.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.2E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant | Internal method | ||
| 1.10 GHz | 3.65 | Internal method | |
| 1.90 GHz | 3.72 | Internal method | |
| Dissipation Factor | Internal method | ||
| 1.10 GHz | 0.013 | Internal method | |
| 1.90 GHz | 0.012 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 - 60 | °C | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 255 - 275 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 100 - 160 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND AU 7200 | POLY GIN | PC+ABS | MARCOBLEND |
| Marlex® 9518H | Chevron Phillips Chemical Company LLC | HDPE, HMW | Marlex® |
| RTP 101 CC HI FR | RTP Company | PP, Unspecified | RTP |
| TAROPRENE® 1 A60 E6N V0 | Taro Plast S.p.A. | TPV | TAROPRENE® |
| 3M™ Dyneon™ Fluoroelastomer FE 5624Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |