Starex HF-0660IW
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aauu93_Starex-HF-0660IW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WNP high flow ABS material |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 39.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Break | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 18 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2200 | MPa | ASTM D790 |
| -- 3 | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 59.0 | MPa | ASTM D790 |
| -- 5 | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 6.35 mm | 200 | J/m | ASTM D256 |
| 23°C 7 | 20 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 88.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 98.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 4.00 mm | 75.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ISO 306/B50 |
| -- | 98.0 | °C | ISO 306/B120 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index (3.20 mm) | 11 to 21 | YI | ASTM D1925 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Desiccant Dryer | 2.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 200 to 210 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 196 | MPa | |
| Back Pressure | 7.85 to 11.8 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex HK4920SN | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| Precision Polymer V76F | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| TRILOY® 170 | Samyang Corporation | PC+PBT | TRILOY® |
| MACOMASS PP MM-PP HK 82 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| Plaslube® PA6 GL10 | Techmer Engineered Solutions | Nylon 6 | Plaslube® |