Chemlon® 66GF6H Datasheet,Nylon 66,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
66GF6H is a 30% glass fibre reinforced, heat stabilised nylon 66 that offers good mechanical performance and endurance at elevated service temperatures, coupled with good surface finish and flow.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer
Features	Good liquidity Thermal Stability Excellent appearance
Uses	High temperature application
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.37	--	g/cm³	ISO 1183
Molding Shrinkage ¹	0.60 - 1.5	--	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	1.8	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	9000	6800	MPa	ISO 527-2
Tensile Stress	180	125	MPa	ISO 527-2
Tensile Strain (Break)	5.0	10	%	ISO 527-2
Flexural Modulus	9000	5100	MPa	ISO 178
Flexural Stress	250	105	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Unnotched Impact Strength	48 kJ/m²	No Break		ISO 179/1eU
Notched Izod Impact	6.0	20	kJ/m²	ISO 180/A

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 240	--	°C	ISO 75-2/B
1.8 MPa, not annealed	240	--	°C	ISO 75-2/A

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+14	1.0E+11	ohms	IEC 60093
Volume Resistivity	1.0E+16	1.0E+13	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	16	--	kV/mm	IEC 60243-1
Comparative Tracking Index	600	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (1.50 mm, Teknor Apex test result)	HB	--		UL 94

Injection	Dry	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Rear Temperature	270 - 290	°C
Middle Temperature	270 - 290	°C
Front Temperature	270 - 290	°C
Processing (Melt) Temp	270 - 290	°C
Mold Temperature	80.0 - 90.0	°C
Injection Rate	Fast
Back Pressure	Low
Screw Speed	Moderate

Injection instructions
No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	a9k9kZ_Chemlon-66GF6H.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RANPELEN SFI-740P	Lotte Chemical Corporation	PP Terpolymer	RANPELEN
ADDINYL B2 ZG30	ADDIPLAST	Nylon 6	ADDINYL
Fluoroplex I 10 - GMP	UNIFLON	PTFE	Fluoroplex
ESPRENE EPDM 522	Sumitomo Chemical Co., Ltd.	EPDM	ESPRENE EPDM
InnoPlus HD1600J	PTT Global Chemical Public Company Limited	HDPE	InnoPlus