TAISOX 7310M
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a7FK9o_TAISOX-7310M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 7310M is an Ethylene Vinyl Acetate Copolymer (EVA) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of TAISOX 7310M are:
Typical application of TAISOX 7310M: Foam |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 6.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 47 98 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 7.85 | MPa | |
| Break | 14.7 | MPa | |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Flexural Modulus | 35.3 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Melting Temperature | 102 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-757G J08 | CHI MEI CORPORATION | ABS | POLYLAC® |
| Ultramid® A3WG7 | BASF Corporation | Nylon 66 | Ultramid® |
| Bergamid™ A700 G40 H (f1) | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Chemlon® 182 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Hifax CJ232 | LyondellBasell Industries | TPO (POE) | Hifax |