VYTEEN ABS 2904
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Lavergne Group |
| Trademark: | VYTEEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q4xywr_VYTEEN-ABS-2904.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vyteen ABS 2904 is a black recycled ABS high impact high flow terpolymer with balanced impact/stiffness properties designed for injection molding applications Features
Typical Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 7.0 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 36.0 | MPa | ASTM D638 |
| Yield | 35.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2100 | MPa | ASTM D790 |
| -- 3 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 62.0 | MPa | ASTM D790 |
| -- 5 | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/eA |
| 23°C | 15 | kJ/m² | ISO 179/eA |
| Notched Izod Impact (23°C) | 170 | J/m | ASTM D256 |
| Dart Drop Impact | ASTM D5420 | ||
| -29°C | 4.00 | J | ASTM D5420 |
| 23°C | 15.0 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 86.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 45 | mm/min | SAE J369 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.30 | % | |
| Rear Temperature | 185 - 195 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Nozzle Temperature | 230 - 240 | °C | |
| Processing (Melt) Temp | 220 - 235 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Injection Pressure: MediumBack Pressure: Medium |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer E60Q | Precision Polymer Engineering Ltd. | EPDM | Precision Polymer |
| EPLAMID 66 GFS 30 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| Jiangsu Sinarise EX9735X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Karina BLUE PVC COMPOUND 800-06/230-A-ERYB (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax TRC 277P S81497 | LyondellBasell Industries | PP Copolymer | Hifax |