Promyde® B30 P2 G50
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a0OqZB_Promyde-B30-P2-G50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde® B30 P2 G50 is a Polyamide 6 injection moulding grade with 50% Glass fibre and heat stabilised. CHARACTERISTICS Promyde B30 P2 G50 is distinguished by high mechanical strength, hardness, rigidity, thermo stability (melting point 220°C), and resistance to hot lubricants and water. Parts made from Promyde B30 P2 G50 have particularly high dimensional stability and creep strength. APPLICATIONS Promyde B30 P2 G50 is used in a wide range of applications where a combination of mechanical properties and thermal resistance is needed. Glass-fibre reinforced grades are suitable for housings, supports, industrial articles and electrical insulating parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.56 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 25.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.40 - 0.45 | -- | % | ISO 294-4 |
| Flow direction | 0.30 - 0.35 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 15600 | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 215 | 150 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 3.0 | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 14000 | 8000 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 340 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | 27 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 95 | 110 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 3 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 1.3E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 5.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 4.20 | 6.30 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | 0.14 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Back Pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zeoforte® ZSC 2195H | Zeon Chemicals L.P. | NBR | Zeoforte® |
| Nipol® SBR 1500 | Zeon Corporation | SBR, Emulsion | Nipol® SBR |
| CoolPoly® E5107 | Cool Polymers, Inc. | PPS | CoolPoly® |
| CP PRYME® Polycarbonate PC100RULUV-10M BT Clear | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Durethan® BKV 140 H2.0 DUS008 900051 | LANXESS GmbH | Nylon 6 | Durethan® |