WPP PP PPH1TF2-Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d1FfCn_WPP-PP-PPH1TF2-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WPP PP PPH1TF2-Black is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. The main characteristics are: heat resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.95 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 35.0 | MPa | ASTM D638 |
| Yield | 33.0 | MPa | ISO 527-2/5 |
| Yield | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 100 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 2 | 2400 | MPa | ASTM D790 |
| -- 3 | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 1.5 | kJ/m² | ISO 179 |
| 23°C | 4.5 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| -40°C | 2.5 | kJ/m² | ISO 180 |
| 10°C | 3.5 | kJ/m² | ISO 180 |
| 23°C | 4.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 125 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 121 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 74.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 76.0 | °C | ISO 75-2/A |
| 1.8 MPa, not annealed | 73.0 | °C | ISO 75-2/Af |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-1000-GFR10 | QTR, Inc. | PC | QR Resin |
| Gallonprene® GP540-9002(n)F | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| KumhoSunny PC/PBT HCB9330G | Shanghai KumhoSunny Plastics Co., Ltd. | PC+PBT | KumhoSunny PC/PBT |
| SD POLYCA™ SD2201W | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| PENTAMID B GK30 H LS black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |