NEALID NW300 - 8229
| Category: | Nylon+PP , Polyamide + PP |
| Manufacturer: | AD majoris |
| Trademark: | NEALID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZzgDy7_NEALID-NW300---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEALID NW300 - 8229 is a 30 % chemically coupled mineral reinforced alloy intended for injection moulding. The base polypropylene has been modified resulting in high performance engineering properties. APPLICATIONS NEALID NW300 - 8229 can be used for technically demanding components such as:
Improved properties of NEALID NW300 - 8229 compared to standard chemically coupled mineral polypropylene compound:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.2 to 1.7 | % | |
| Water Absorption (23°C, 24 hr) | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 15 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2800 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.5 | kJ/m² | |
| 23°C | 3.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 143 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 110 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | ohms·cm | DIN 53482 |
| Dielectric Constant | 3.00 | DIN 53483 | |
| Dissipation Factor (1 kHz) | 0.030 | DIN 53483 | |
| Comparative Tracking Index | > 600 | V | DIN 53480 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 255 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer J-700 | Shanghai Potomer International Trade Co., Ltd. | CPVC | Shanghai Potomer |
| AMTOPP WT30 | Inteplast Group | PP, Unspecified | AMTOPP |
| Guang Sung PVC GPMA90 | Guang Sung Plastics (GSPL) | PVC, Flexible | Guang Sung PVC |
| Karina GRAY PVC COMPOUND 732D18/87-G-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| EPAMOULD 760D15 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPAMOULD |