MALAT 37N007 - 8689
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | AD majoris |
| Trademark: | MALAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZyiHKc_MALAT-37N007---8689.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MALAT 37N007 - 8689 is a polybutylene terephthalate , intended for injection moulding. The product is available in natural and black (MALAT 37N007 - 8229) but other colours can be provided on request They combine high mechanical, thermal and electrical properties with excellent chemical resistance. APPLICATIONS MALAT 37N007 - 8689 is intended for the injection moulding of electrical components and automotive applications including interior, exterior and electrical and mechanical systems, such as:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1(3.00 mm) | 1.5 - 2.0 | % | |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 34.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 55 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress 2 | 205 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Ball Pressure Test (200°C) | Pass | NF C 62-411 | |
| Melting Temperature (DSC) | 225 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 23 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.00 | ASTM D150 | |
| 1 kHz | 3.00 | ASTM D150 | |
| 1 MHz | 2.90 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ASTM D150 | |
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 7.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm, 30 sec) | 650 | °C | IEC 60695-2-13 |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 245 - 260 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Back pressure: Moderate |
| Note Message | |
|---|---|
| 1 . | Plate 100x100x3 mm |
| 2 . | at Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® G black EL | Röchling Engineering Plastics SE & Co. KG | HDPE | POLYSTONE® |
| S&E PVC GPT-76-1 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Advanced Composites ATX832D | Advanced Composites, Inc. | TPO | Advanced Composites |
| EMPILON® 590 | EMPILON | SEBS | EMPILON® |
| LNP™ LUBRILOY™ D2000I compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |