LNP™ COLORCOMP™ G1000 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZyKc0E_LNPCOLORCOMPG1000compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP COLORCOMP G1000-GY4A805-0 is a compound based on Polysulfone resin. Added features include: Custom Color Grey. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 76.0 | MPa | ISO 527-2/50 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.9 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 183 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 170 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 6.2E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 - 338 | °C | |
| Middle Temperature | 338 - 349 | °C | |
| Front Temperature | 349 - 360 | °C | |
| Processing (Melt) Temp | 360 - 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCS-2207HE | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Durez® 33609 | Durez Corporation | Phenolic | Durez® |
| Hostacom M4 U05 102943 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Plaslube® PSU GF20 TL5 | Techmer Engineered Solutions | PSU | Plaslube® |
| Thermec N™ 4340R35F4 | Technical Polymers, LLC | PPA | Thermec N™ |