Generic SEBS
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2gIsZS_Generic-SEBS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic SEBS This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.886 - 1.23 | g/cm³ | ASTM D792 |
| 23°C | 0.888 - 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.50 - 14 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.10 - 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.29 - 2.6 | % | ASTM D955 |
| Transverse flow : 23°C | 0.73 - 1.8 | % | ASTM D955 |
| 23°C | 1.4 - 2.4 | % | ISO 294-4 |
| Bound Styrene | 29.7 - 33.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 29 - 90 | ASTM D2240 | |
| 23°C | 19 - 91 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 0.624 - 4.68 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 3.17 - 5.82 | MPa | ASTM D638 |
| Fracture, 23°C | 3.00 - 28.0 | MPa | ISO 527-2 |
| 23°C | 0.100 - 7.48 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 490 - 600 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 640 - 850 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (23°C) | 0 - 8 | % | ASTM D412 |
| Tensile Stress | |||
| 50% strain, 23°C | 0.241 - 3.10 | MPa | ASTM D412 |
| 100% strain, 23°C | 0.0900 - 3.78 | MPa | ASTM D412 |
| 100% strain, 23°C | 0.300 - 5.66 | MPa | ISO 37 |
| 200% strain, 23°C | 0.500 - 6.26 | MPa | ISO 37 |
| 300% strain, 23°C | 0.843 - 5.31 | MPa | ASTM D412 |
| 300% strain, 23°C | 0.890 - 6.78 | MPa | ISO 37 |
| Tensile Strength | |||
| Yield, 23°C | 2.07 - 12.6 | MPa | ASTM D412 |
| Yield, 23°C | 1.66 - 11.1 | MPa | ISO 37 |
| Fracture, 23°C | 2.00 - 12.6 | MPa | ASTM D412 |
| Fracture, 23°C | 4.94 - 22.2 | MPa | ISO 37 |
| 23°C | 1.18 - 15.6 | MPa | ASTM D412 |
| Tensile Elongation | |||
| Yield | 980 - 1400 | % | ASTM D412 |
| Fracture, 23°C | 500 - 1000 | % | ASTM D412 |
| Fracture, 23°C | 290 - 880 | % | ISO 37 |
| Tear Strength | |||
| 23°C | 9.73 - 52.3 | kN/m | ASTM D624 |
| 23°C | 11 - 45 | kN/m | ISO 34-1 |
| Compression Set | |||
| -- | 8.3 - 87 | % | ASTM D395 |
| 23°C | 9.0 - 47 | % | ISO 815 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -55.7 - -39.1 | °C | ASTM D746 |
| Melting Temperature (DSC) | 151 - 166 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 70.0 - 92.4 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.1 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 160 - 182 | °C | |
| Middle Temperature | 168 - 201 | °C | |
| Front Temperature | 175 - 223 | °C | |
| Nozzle Temperature | 180 - 210 | °C | |
| Processing (Melt) Temp | 187 - 252 | °C | |
| Mold Temperature | 26.6 - 50.1 | °C | |
| Injection Pressure | 3.43 - 53.1 | MPa | |
| Back Pressure | 0.421 - 3.50 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic SEBSThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 1.9 - 3.0 | hr | |
| Cylinder Zone 1 Temp. | 159 - 172 | °C | |
| Cylinder Zone 2 Temp. | 165 - 181 | °C | |
| Cylinder Zone 3 Temp. | 174 - 200 | °C | |
| Cylinder Zone 4 Temp. | 189 - 196 | °C | |
| Cylinder Zone 5 Temp. | 194 - 205 | °C | |
| Adapter Temperature | 180 - 190 | °C | |
| Die Temperature | 185 - 210 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic SEBSThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom EP5140 | Spartech Polycom | PP Homopolymer | Spartech |
| SUPREME Specialty PS SP253 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| Moplen HP493M | LyondellBasell Industries | PP Homopolymer | Moplen |
| Arnite® A06 101 | DSM Engineering Plastics | PET | Arnite® |
| Plaslube® PC-50/TF/13/SI/2 BK3585 | Techmer Engineered Solutions | PC | Plaslube® |