Latene® 22H2 MX/25
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZkZyeY_Latene-22H2-MX-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polypropylene homopolymer (PPh). Heat stabilised. Special mineral filler. Product UL certified. Very good surface appearance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.2 to 1.5 | % | |
| Flow : 2.00 mm | 1.1 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2600 | MPa | |
| 60°C | 1100 | MPa | |
| 90°C | 650 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 25.0 | MPa | |
| Yield, 60°C | 20.0 | MPa | |
| Yield, 90°C | 10.0 | MPa | |
| Break, 23°C | 18.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 6.0 | % | |
| Yield, 60°C | 9.0 | % | |
| Yield, 90°C | 9.0 | % | |
| Break, 23°C | 140 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 1.0 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 15 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 750 | °C | |
| 2.00 mm | 750 | °C | |
| Oxygen Index | 24 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1800 UV | RTP Company | Acrylic (PMMA) | RTP |
| Radilon® BHZL 200 Black | Radici Plastics | Nylon 6 | Radilon® |
| Fainplast PVC RKS 325 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Hanwha Total PP TB52L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| MAXAMID™ EPDM0366-BK | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |