LG ABS HI100
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2uqnZq_LG-ABS-HI100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS HI100 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of LG ABS HI100 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 1610 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 37.3 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20mm | > 5.0 | % | ASTM D638 |
| Fracture, 3.20mm | 30 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 1810 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 57.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 270 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 270 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 440 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 420 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 84.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 6 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 190 - 210 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G20 291 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Spartech Polycom SC7-7010RF | Spartech Polycom | PC | Spartech |
| TAROMID A 280S | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Hostalen PP H4122 103220 | LyondellBasell Industries | PP Copolymer | Hostalen PP |
| Sylvin 8915-90 UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |