RTP 2800B-40A HF
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZhDELP_RTP-2800B-40A-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm, Injection Molded) | 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 40 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 3.00 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 450 | % | ASTM D412 |
| Tear Strength 1 | 11.0 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 to 199 | °C | |
| Middle Temperature | 171 to 199 | °C | |
| Front Temperature | 171 to 199 | °C | |
| Mold Temperature | 16.0 to 66.0 | °C | |
| Injection Pressure | 83.0 to 124 | MPa |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Crystal 1160 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Nycal™ 2150T1 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| HiFill FR® PA6/6,6 FR NAT | Techmer Engineered Solutions | Nylon 66/6 | HiFill FR® |
| KARIPRENE NATURAL 6125/ 1-RTR | Karina Ind. e Com. de Plásticos Ltda | TPE | KARIPRENE |
| LinGen FR600 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP, Unspecified | LinGen |