SABIC® PPcompound 8501
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZcxyIe_SABICPPcompound8501.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8501 is an elastomer-modified mineral filled Polypropylene for automotive painted exterior applications. Its low density and excellent stiffness impact balance makes it suited for weight reduction designs. Typical applications include automotive exterior parts such as zero gap automotive bumper applications with complex and large shapes. SABIC® PPcompound 8501 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.0 - 1.1 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield, injection molding | 18.0 | MPa | ISO 527-2/1A/50 |
| Fracture, injection molding | 12.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break, Injection Molded) | 100 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1(Injection Molded) | 1250 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Notched Izod Impact | ISO 180/4A | ||
| -20°C, injection molding | 10 | kJ/m² | ISO 180/4A |
| 0°C, injection molding | No Break | ISO 180/4A | |
| 23°C, injection molding | No Break | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 98.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 128 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.5E-5 | cm/cm/°C | ASTM D696 |
| 23 to 80°C | 9.5E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 B TFE 15 | RTP Company | Nylon 610 | RTP |
| Wellamid® MRGF3820-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| NANCAR® 70.30 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| Geon™ Vinyl Rigid Extrusion L0248 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Sylvin 9077-85 White 1315 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |