Order Products : sales@su-jiao.com
Loyblend® TA-1840FR
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Loyblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XV4sNa_Loyblend-TA-1840FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Loyblend® TA-1810FR is non-chlorinated, non-brominated flame retardant PC/ABS alloy compound. This grade offers high flow and high gloss surface. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 60 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2970 | MPa | ASTM D638 |
| Tensile Strength | 59.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 30 | % | ASTM D638 |
| Flexural Modulus 1 | 2550 | MPa | ASTM D790 |
| Flexural Strength 2 | 94.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 87.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1.4 mm/min |
| 2 . | 1.4 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 1825-UV | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Baoding 76I85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| Evoprene™ GC 5683 | AlphaGary | SEBS | Evoprene™ GC |
| Estane® 2103-80AE TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| SHINSTRA WG25TKB | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |