Polypropylene Heterophasic Copolymer

Characteristics

The KPOL® resin is a propylene impact copolymer designed for injection molding applications, Excellent Balance of Stiffness and Impact Strength at low temperatures, Contains Nucleating , Good Mold Release.

Superior Drop Impact at Refrigeration Temperature, Very High Flexural Modulus. Also is suitable for technical components: toys, sports, equipment, leisure goods, automotive, pallets, crates and pails.

Applications

Injection / Automobile applications, Battery case, Home appliances, Industrial parts for electronic.

Thermoformed packages with high impact strength; Blown packages and technical parts in general.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant BPA Free Good Impact Resistance Good Mold Release Good Stiffness Impact Copolymer Low Temperature Resistant Nucleated
Uses	Appliances Automotive Applications Battery Cases Crates Electrical/Electronic Applications Industrial Parts Packaging Pallets Thermoforming Applications Toys
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Blow Molding Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	3.5	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	68		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	23.0	MPa	ASTM D638
Tensile Elongation ²(Break)	8.0	%	ASTM D638
Flexural Modulus - 1% Secant	1100	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (-20°C)	72	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	87.0	°C	ASTM D648
Vicat Softening Temperature	154	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
MARPOL® HDM 520	Marco Polo International, Inc.	HDPE	MARPOL®
Nucrel® 699	DuPont Packaging & Industrial Polymers	EMAA	Nucrel®
ACRYLITE® Sheet 249	Evonik Cyro LLC	Acrylic (PMMA)	ACRYLITE® Sheet
Baoding 65E70	Baoding Bangtai Polymeric New-Materials Co.,Ltd	TPU-Polyether	Baoding
Sylvin 3200-85 Clear	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin