Petrotene® PP T3 CINZA 7743 SB28 PH341
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Gq2b2l_Petrotene-PP-T3-CINZA-7743-SB28-PH341.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene loaded with talc 28% barium sulfate for injection molding, good set of mechanical properties and good dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 to 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 to 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 22.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 28 | % | ASTM D638 |
| Flexural Modulus | 1960 | MPa | ASTM D790 |
| Flexural Strength | 44.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 3 | ASTM D648 | ||
| 0.45 MPa, Unannealed | 130 | °C | |
| 1.8 MPa, Unannealed | 70.0 | °C | |
| Continuous Use Temperature | 80.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 90.0 | °C | ASTM D1525 4 |
| -- | 134 | °C | ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2°C/min |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E380PKOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Sylvin 9302-75FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TITANPRO® PD701 | Lotte Chemical Titan (M) Sdn. Bhd. | PP Homopolymer | TITANPRO® |
| TIPPLEN® H 681 F | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| Tunhe PBS TH803S | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBS | Tunhe PBS |