Hanwha Total PP BI970
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZaS51O_Hanwha-Total-PP-BI970.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BI970 is a highly isotactic block copolymer with ultra-high flowability, high impact, and higher crystalinity compared to general PP. It maintains an optimum balance of strength and impact resistance due to high crystalline technology and the most appropriate rubber design. Through the control of molecular weight distribution, the product shows superior melt flow compared to normal PP and is appropriate for energy savings and multi-cavity injection molding. BI970 is useful in large scale thin products with low distortion tendencies and may also be used as a compound base resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 100 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 31.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 1670 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 125 | °C | ASTM D648 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss | 85 | ASTM D2457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 160 - 200 | °C | |
| Middle Temperature | 200 - 240 | °C | |
| Front Temperature | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Pressure | 98.1 - 245 | MPa | |
| Holding Pressure | 78.5 - 226 | MPa |
| Injection instructions |
|---|
| Cooling Time: 25 to 40 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3576 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Dylite® F271C | NOVA Chemicals | PS (EPS) | Dylite® |
| HiFill® PA6/6 GF30 RM-1 L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Petrothene® LR7810 | LyondellBasell Industries | HDPE | Petrothene® |
| Badatech HT® PEEK 3111 GF 30 | Bada AG | PEEK | Badatech HT® |