Sarlink® TPE EE-2263N
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZBhbGl_Sarlink-TPE-EE-2263N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE EE-2263N is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: extrusion. Sarlink®The typical application field of TPE EE-2263N is: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 69 | ASTM D2240 | |
| Shaw A, 15 seconds | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 37.9 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain | 1.86 | MPa | ASTM D412 |
| Flow : 100% strain | 2.62 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Transverse flow : Fracture | 8.41 | MPa | ASTM D412 |
| Flow : Fracture | 5.93 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Transverse flow : Fracture | 810 | % | ASTM D412 |
| Flow : Fracture | 660 | % | ASTM D412 |
| Tear Strength - Across Flow | 30.8 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 20 | % | ASTM D395 |
| 70°C, 22 hr | 37 | % | ASTM D395 |
| 125°C, 70 hr | 73 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 168 hr) | -7.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (100°C, 168 hr) | -2.0 | % | ASTM D573 |
| Change in Durometer Hardness in Air 1(Shore A) | 1.0 | ASTM D573 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(2.03 mm) | 51 | mm/min | ISO 3795 |
| Additional Information |
|---|
| 可燃性燃烧速率 (FMVSS 302) 2.0英寸/分钟= 合格 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Points |
| 2 . | (FMVSS 302) = PASS |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mecoline IS RDX 1207 F | Melos GmbH | TP, Unspecified | Mecoline |
| ShinkoLite-P IR D-30 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| Nypol® PA A3 Z40 HS NTLA010 NR457 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Delta ATR-1G50 | Delta Polymers | Acetal (POM) Homopolymer | Delta |
| ICORENE® N4506 | ICO Polymers EMEA, A Division of A. Schulman | PP Random Copolymer | ICORENE® |