DOWLEX™ 2107B
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z9nOAa_DOWLEX-2107B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2107B Polyethylene Resin with Extra Stretch Performance is an Ethylene-1-Octene copolymer designed for cast film applications, such as industrial pallet wrap. DOWLEX 2107B provides stretch film with superior extensibility and increased resistance to failure around film flaws while maintaining exceptional puncture resistance and load retention. Main Characteristics:
Complies with:
Suitable for food contact, Report # 927/09 issued by INAL according to MERCOSUR. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.6 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance (22 µm) | 157 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 22 µm | 189 | MPa | ASTM D882 |
| 2% secant, TD : 22 µm | 196 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 22 µm | 10.9 | MPa | ASTM D882 |
| TD : Yield, 22 µm | 10.8 | MPa | ASTM D882 |
| MD : Break, 22 µm | 30.3 | MPa | ASTM D882 |
| TD : Break, 22 µm | 28.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 590 | % | ASTM D882 |
| TD : Fracture | 870 | % | ASTM D882 |
| Dart Drop Impact (22 µm) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 22 µm | 160 | g | ASTM D1922 |
| TD : 22 µm | 710 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 22.0 µm) | 78 | ASTM D2457 | |
| Haze (22.0 µm) | 5.2 | % | ASTM D1003 |
| Additional Information |
|---|
| 22 um 薄膜挤出铸造的推荐加工条件： 熔体温度：220 - 280C 冷却辊温度：15 - 60C 生产线速度：150 - 600 米/分 厚度：10 - 60 微米 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTAL PM1113 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| THERMOLAST® K TP4CDZ (Series: EX) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Kepital® FC2020D | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| PLUSTEK PA840G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Starex LX-0760 | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |