Andur AL 80-5 AP/Curene® 111
| Category: | PUR-Eth,aliphat , Polyurethane (Polyether, Aliphatic) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MfqE9z_Andur-AL-80-5-AP-Curene-111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur AL80-5AP is a polyether (PTMG) based prepolymer terminated with an aliphatic isocyanate to improve color stability, hydrolytic stability, and give longer pot life. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 82 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 5.45 | MPa | ASTM D412 |
| 300% strain | 15.8 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 35.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Compression Set | 55 | % | ASTM D395B |
| Bayshore Resilience | 40 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 7.0 | min | |
| Demold Time (100°C) | 30 | min | |
| Post Cure Time | |||
| 21°C | 72 | hr | |
| 100°C | 16 | hr |
| Additional Information |
|---|
| Die C Tear, ASTM D1004: 290 pliAverage Split Tear, ASTM D1938: 75 pliStoichiometry Curative Level: 95%Mix Temperature: Andur AL 80-5 AP: 158°F Curene 111: 72°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNFROST® KA75GA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| Ad-Tech Epoxy EC-413 Medium LP | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Axiall PVC 19853 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| CONTINUUM™ DGDA-2490 BK | The Dow Chemical Company | HDPE | CONTINUUM™ |
| Fainplast PVC RKI 713/UV | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |