EPLAMID 6 CFR 10 NC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z1C2uM_EPLAMID-6-CFR-10-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66, reinforced with 10 % of carbon fiber, heat stabilized, lubricated for injection moulding. Eplamid 6 CFR 10 is used in all sectors of industry, offering a perfect balance of thermal and mechanical properties. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 - 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 3.00mm | 0.80 | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.30 | % | ISO 294-4 |
| Moisture Content | 0.20 | % | ISO 15512 |
| Ash content- CARBON FIBER (550°C -10 min) | 10.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 84 - 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6000 - 7000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 105 - 145 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 - 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5500 - 6000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 90.0 - 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 - 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 6.0 - 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 200 - 230 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 380.5 FR | RTP Company | PC | RTP |
| AKROMID® A3 GK 30 natural (3689) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Excelprene® 8375 RoHS | S&E Specialty Polymers, LLC | PVC, Flexible | Excelprene® |
| KumhoSunny PBT 3730FG | Shanghai KumhoSunny Plastics Co., Ltd. | PBT | KumhoSunny PBT |
| Plexiglas® VS-UVT | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |