Sumitomo Phenolic FM 4004F
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Phenolic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YOBBNN_Sumitomo-Phenolic-FM-4004F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM 4004F is a fiberglass and mineral reinforced phenolic novolac compound with improved strength properties over FM 4004. This compound exhibits excellent dimensional stability and good strength at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.88 | g/cm³ | ASTM D792 |
| Apparent Density | 0.98 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.23 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Water Absorption - 48 hr | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale, Compression Molded) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Compression Molded) | 80.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 17100 | MPa | ASTM D790 |
| Flexural Strength (Compression Molded) | 115 | MPa | ASTM D790 |
| Compressive Strength | 230 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 29 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, Compression Molded | 185 | °C | |
| 1.8 MPa, Annealed, Compression Molded | > 282 | °C | |
| CLTE - Flow | 1.9E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI Str | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 16 | kV/mm | |
| -- 3 | 14 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 4.60 | ASTM D2520 | |
| Dissipation Factor 5(1 MHz) | 0.012 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 MG 20 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Bapolan® ABS8430 | Bamberger Polymers, Inc. | ABS | Bapolan® |
| Lushan M-1 | Guangzhou Lushan New Materials Co., Ltd | Polyolefin, Unspecified | Lushan |
| Sylvin 8376-92UV Yellow 4209 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ 103R resin | SABIC Innovative Plastics | PC | LEXAN™ |