LNP™ LUBRICOMP™ RBL36XXJ compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lZoAU9_LNP-LUBRICOMP-RBL36XXJ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RBL36XXJ is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features of this grade include: Low Extractable, Healthcare, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RBL-4036 HC LE Product reorder name: RBL36XXJ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.41 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.58 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3990 | MPa | ASTM D638 |
| -- | 3930 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 64.0 | MPa | ASTM D638 |
| Break | 64.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 8.5 | % | ASTM D638 |
| Break 4 | 10 | % | ASTM D638 |
| Break | 8.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 3740 | MPa | ASTM D790 |
| -- 6 | 3570 | MPa | ISO 178 |
| Flexural Stress | 107 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.47 | ||
| vs. Itself - Static | 0.44 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 8.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 41.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 51 | J/m | ASTM D256 |
| 23°C 7 | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 8 | 27 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.60 | J | ASTM D3763 |
| -- | 1.34 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 236 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 203 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 83.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 73.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SBC3707 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sinpolene MBB206 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| ADENE NCJA | A.D. Compound spa | PP Homopolymer | ADENE |
| Hanwha Total PP FH44 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| PETLIN LD N109X | PETLIN (MALAYSIA) SDN BHD | LDPE | PETLIN |