STYRON™ C-TECH HIPS
| Category: | PS (HIPS) , High Impact Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON™ C-TECH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YLXmUp_STYRON-C-TECH-HIPS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON™ C-TECH is a high clarity, high gloss polystyrene with excellent mechanical properties on thermoformed parts. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.3 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm 1 | 2700 | MPa | ASTM D638 |
| 3.20 mm | 2700 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield, 3.20 mm 2 | 33.0 | MPa | ASTM D638 |
| Yield, 3.20 mm | 33.0 | MPa | ISO 527-2/5 |
| Break, 3.20 mm 3 | 27.0 | MPa | ASTM D638 |
| Break, 3.20 mm | 27.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break, 3.20 mm 4 | > 20 | % | ASTM D638 |
| Break, 3.20 mm | > 20 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 3.20 mm 5 | 2600 | MPa | ASTM D790 |
| 3.20 mm | 2600 | MPa | ISO 178 |
| Flexural Strength | |||
| 3.20 mm 6 | 62.0 | MPa | ASTM D790 |
| 3.20 mm | 62.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 72.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/A120, ASTM D1525 7 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 8(1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Thermoformed) | 60 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | Method I (3 point load), 1.3 mm/min |
| 6 . | Method I (3 point load), 1.3 mm/min |
| 7 . | Rate B (120°C/h), Loading 1 (10 N) |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PE HD0790 | Qenos Pty Ltd | HDPE | Qenos PE |
| MIDILENA I LDPE B21/2 | ROMPETROL PETROCHEMICALS S.R.L. | LDPE | MIDILENA I |
| Sinvicomp SBF3758 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sumitomo Epoxy E 8701A | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| Taitarex® 861N / B / W | Taita Chemical Company, Ltd. | PS (GPPS) | Taitarex® |