SABIC® PPcompound 6612
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YLTkcV_SABIC-PPcompound-6612.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC®PPcompound 6612 is a polypropylene product that contains mineral fillers. It can be processed by injection molding and is available in Europe. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 19 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 85 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20mm | 17.0 | MPa | ISO 527-2/5/50 |
| Fracture, 3.20mm | 17.0 | MPa | ISO 527-2/5/50 |
| Tensile Strain (Break, 3.20 mm) | 500 | % | ISO 527-2/5/50 |
| Flexural Modulus 1 | 1350 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (-40°C) | 80 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180/3A | ||
| -40°C | 3.0 | kJ/m² | ISO 180/3A |
| -20°C | 5.0 | kJ/m² | ISO 180/3A |
| 0°C | No Break | ISO 180/3A | |
| 23°C | No Break | ISO 180/3A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 95.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 115 | °C | ISO 306/A50 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Mold Shrinkage, SABIC Method: 0.7% |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAMID® L LX9102 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| Ferro PP LPP40BD25GY | Ferro Corporation | PP Homopolymer | Ferro PP |
| Durepol® PBT A3 G20 BRCA010 BT325 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| HiFill FR® PA6/6 GF50 FR-N BK | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |
| Microthene® MP652962 | LyondellBasell Industries | HDPE | Microthene® |