Durethan® AKV 15 FN 00 000000
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YK9sRs_Durethan-AKV-15-FN-00-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 12 % glass fibers, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.28 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (270°C/2.16 kg) | 25.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 270°C, 2.00 mm 1 | 1.0 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | -- | % | |
| Flow : 270°C, 2.00 mm 3 | 0.60 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6500 | 3600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 90.0 | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.3 | 5.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 6400 | 3300 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 150 | 90.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.3 | 5.5 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GFHR, 14-060, GF12 ISO 1043:PA GF FR (30+40) | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 40 | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 35 | 40 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 225 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 262 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 0 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm | V-0 | -- | ||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| 3.00 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.400 mm | 960 | -- | °C | |
| 0.800 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 265 to 285 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4297 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| VITAMIDE® AR15 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| NAXALOY® 770-BK272 | MRC Polymers, Inc. | PC+ABS | NAXALOY® |
| KOCETAL® GF305LOBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Karina CLEAR PVC COMPOUND -E 75/316-IS-RG (GLASS CLEAR) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |