Stanyl® TW278F10
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y3BVeo_Stanyl-TW278F10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TW278F10 is a Polyamide 46 (Nylon 46) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of Stanyl® TW278F10 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 225 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 285 | °C | ISO 75-2/A |
| Melting Temperature | 290 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC G-2100-80 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| REPOL® R120MK | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| XYRON™ G703V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| ColorFast® NYA1000 | LTL Color Compounders, Inc. | ABS+Nylon | ColorFast® |
| LNP™ THERMOCOMP™ Lexan_LGK3020 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |