ULTEM™ 4002 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y1AIGf_ULTEM-4002-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL 94 V0 and 5VA listing in recognized colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 9.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.60 to 0.80 | % | |
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.1 | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3460 | MPa | ASTM D638 |
| -- | 3300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 105 | MPa | ASTM D638 |
| Yield | 100 | MPa | ISO 527-2/50 |
| Break 4 | 85.0 | MPa | ASTM D638 |
| Break | 80.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 5.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 6 | 40 | % | ASTM D638 |
| Break | 25 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 3550 | MPa | ASTM D790 |
| -- 8 | 3100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 130 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 120 | J/m | ASTM D256 |
| 23°C | 120 | J/m | ASTM D256 |
| -30°C 11 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 380 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 197 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 200 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 13 | 190 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 219 | °C | ASTM D1525 14 |
| -- | 215 | °C | ISO 306/B50 |
| -- | 210 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 150°C | 3.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 150°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 338 to 360 | °C | |
| Middle Temperature | 343 to 366 | °C | |
| Front Temperature | 349 to 371 | °C | |
| Nozzle Temperature | 349 to 371 | °C | |
| Processing (Melt) Temp | 349 to 371 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU H895FNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Trexprene® A55NI-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| ColorRx® ACR-0400RX | LTL Color Compounders, Inc. | Acrylic, Unspecified | ColorRx® |
| Sylvin 6197A-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CYCOLAC™ MG47U resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |