Task® 7 - Flame Out®
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Task® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xs4etY_Task-7---Flame-Out-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame Out® is a low viscosity, fast set casting resin that meets UL 94 V-O requirements for flame resistance. It does not contain mercury, TDI or MOCA. Mix ratio is 1A:1B by volume. Pot life is 2.5 min. and demold time is 10 min. at 73°F / 23°C (depending on mass). Fully cured Flame Out® material is tough, durable, machinable and paintable. It has much higher physical and performance properties than any other flame rated urethane available anywhere. Vibrant colors and color effects are possible by adding SO-Strong® color tints. Applications for Flame Out® include making flame resistant prototype and architectural models, model toys, theme park and stage elements, durable miniatures and special effect props. Material can also be used for potting and encapsulation applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.835 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 1A:1B by volume |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 1.1 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1040 | MPa | ASTM D638 |
| Tensile Strength (Break) | 23.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790 |
| Flexural Strength | 37.6 | MPa | ASTM D790 |
| Compressive Modulus | 397 | MPa | ASTM D695 |
| Compressive Strength | 35.4 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 55.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 2.5 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 200 | cP | ASTM D2393 |
| Demold Time 1(23°C) | 10 | min |
| Note Message | |
|---|---|
| 1 . | Cure Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax RP491S | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| TOTAL Polypropylene PPC 7642 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| APEX® 80853-C Nat 14 | Teknor Apex Company | PVC, Flexible | APEX® |
| MACOMASS TPE MM-TPE V 3140 | MACOMASS Verkaufs AG | TPE | MACOMASS TPE |
| Sylvin 8225-95UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |