Starex GR-4005
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xr9fpE_StarexGR4005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex GR-4005 is an acrylonitrile butadiene styrene (ABS) product, which contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: commercial/office supplies. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| natural color | 1.08 | g/cm³ | ASTM D792 |
| natural color | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 15 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 - 0.40 | % | ASTM D955 |
| Ash Content | 5.2 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 110 | ASTM D785 | |
| R scale | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2940 | MPa | ASTM D638 |
| -- | 3100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 58.8 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 47.1 | MPa | ASTM D638 |
| Fracture | 54.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 3.6 | % | ASTM D638 |
| Fracture | 3.3 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 3040 | MPa | ASTM D790 |
| -- | 3300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 6 | 87.3 | MPa | ASTM D790 |
| -- | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 9.1 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 70 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 71 | J/m | ASTM D256 |
| 23°C 8 | 7.6 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 103 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 100 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 89.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/B50 |
| -- | 106 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | HB | UL 94 | |
| 1.8 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 - 230 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 240 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Pressure | 49.0 - 245 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | Thickness: 4mm |
| 8 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVALAC RX®831 | Vyncolit N.V. | Phenolic | NOVALAC |
| Delrin® 100ST NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Petrothene® NA340141 | LyondellBasell Industries | LDPE | Petrothene® |
| Wanthane® WHT-1172IC | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| LNP™ THERMOCOMP™ PF006U compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |