Lotryl® 30BA02
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotryl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YpQ3iY_Lotryl-30BA02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTRYL® 30BA02 is a random copolymer of Ethylene and Butyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to the high butyl acrylate content, LOTRYL® 30BA02 can be used for applications where flexibility and polarity are required. LOTRYL® 30BA02 can be used for polymer modification, in compounds formulations and in film applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 to 2.5 | g/10 min | ASTM D1238, ISO 1133 |
| n-Butyl Acrylate Content | 28.0 to 32.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 75 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 6.00 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 850 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 9.00 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 41.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 75.0 | °C | ISO 11357-3 |
| Ring and Ball Softening Point | < 190 | °C | ASTM E28 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Die Temperature | 170 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIM6039 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| NEXUS Reprocessed Nylon 66 G33 RBK | Nexus Resin Group, LLC. | Nylon 66 | NEXUS Reprocessed |
| Formolene FORMAX® L71709H | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene FORMAX® |
| HiFill® PA6 0254 B2 | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Huafon JF-W-3040 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |