| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XpoUwX_Zytel73G40TBK416.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Glass Reinforced, Toughened, Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.44 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.50 | -- | % | ISO 294-4 |
| Flow | 0.10 | -- | % | ISO 294-4 |
| Water Absorption 1 | ISO 62 | |||
| Saturated, 23°C, 2.00mm | 5.3 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12500 | 8040 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 210 | 147 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.8 | 6.9 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | 14 | kJ/m² | ISO 179/1eA |
| 23°C | 19 | 23 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 2(23°C) | 110 | 120 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 220 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 270 | °C | |
| Mold Temperature, Optimum | 100 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Viscosity (280°C, 1000 sec^-1) | 190000 | -- | mPa·s | ISO 11443 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 70 - 120 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | Derived from Similar Grade |
| 2 . | Derived from Similar Grade |
| 3 . | 10°C/min |
| 4 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-1585 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Estane® AG 8451 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Hypro® PP-CP 50/2 | Entec Polymers | PP Copolymer | Hypro® |
| Kumho KNB 3430G | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| Magnobond 2004 | Magnolia Plastics, Inc. | Epoxy | Magnobond |