Karina NATURAL PVC COMPOUND 900-25/ 1-AYR-IS-LMP (*)
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Kv4fwg_Karina-NATURAL-PVC-COMPOUND-900-25-1-AYR-IS-LMP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND RECOMMENDED FOR INSULATION OF AUTOMOTIVE WIRES. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.27 to 1.33 | g/cm³ | ASTM D792 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -0.210 to 2.79 | ME 12 | |
| Color b | 11.4 to 14.4 | ME 12 | |
| Color L | 84.8 to 87.8 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 88 to 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 14.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 250 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 14.7 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 250 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -29.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 136°C |
| 3 . | Aged in Air for 168 hr at 136°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203H CF 15 | RTP Company | Nylon 66 | RTP |
| RTP 2200 AR 15 TFE 15 | RTP Company | PEEK | RTP |
| SABIC® HDPE F0863 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Kaneka MUH BM5600 | Kaneka Corporation | ABS | Kaneka MUH |
| PENTAMID A GV30 H MOS ungefärbt | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |