MARCOBLEND 2000
| Category: | PC , Polycarbonate |
| Manufacturer: | POLY GIN |
| Trademark: | MARCOBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xm3gFt_MARCOBLEND-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MARCOBLEND 2000 is an ignition resistant and glass fiber reinforced polycarbonate resin. The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, good stiffness, and excellent dimension stability and suitable for use in TFT LCD frame and internal structure parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 69.0 | MPa | ASTM D638 |
| Flexural Modulus | 3390 | MPa | ASTM D790 |
| Flexural Strength | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 145 | °C | |
| 1.8 MPa, Unannealed | 127 | °C | |
| CLTE | ASTM D696 | ||
| Flow | 4.0E-5 | cm/cm/°C | |
| Transverse | 6.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 260 to 265 | °C | |
| Middle Temperature | 265 to 270 | °C | |
| Front Temperature | 270 to 275 | °C | |
| Nozzle Temperature | 275 to 280 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 UV L | RTP Company | PC | RTP |
| Celcon® MC270-HM | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| ESENTTIA 11H01-R2 | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| ESPRENE EPDM 5206F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Sumiliteresin® PR-55291 | SBHPP | Phenolic | Sumiliteresin® |